X6 CrTi 12
|
|
|
Introduction:
Low carbon chromium steels are ferritic and cannot
be hardened other than by cold work. Their yield and
tensile strength properties are similar to 18Cr10Ni
grades but their ductility and impact resistance are
generally much inferior. Some cold forming operations
are also more difficult. Minimum impact values are
not included in Euronorm or ASTM and are subject to
agreement.
X 6 CrTi 12 has a ductile-brittle transition temperature
near or above room temperature and that of its coarse
grained weld zones is higher. Very low carbon versions
give some improvement.
This steel is slow rusting and subject to pitting
and crevice corrosion in aerated seawater. Scaling
temperatures are in the region of 750-800°C.
Composition:
| Element |
Minimum
(%) |
Maximum
(%) |
| Chromium |
10.50 |
12.50 |
| Nickel |
- |
1.00 |
| Manganese |
- |
1.00 |
| Carbon |
- |
0.08 |
| Titanium |
6
x C |
1.10 |
|
Similiar Specifications:
ISO 4955 H1
ISO 683/13 1 Ti
10.5-12.5%Cr, <1%Ni, <1%Mn, <0.08%C, 6 x
C-1.0%Ti
EURONORM X6 CrTi 12
10.5-12.5%Cr, <1.0%Ni, <1.0%Mn, <0.08%C,
6 x %C-1.1%Ti
ASTM UNS S40900 409
10.5-11.75%Cr, <0.5%Ni, <1.0%Mn, <0.08%C,
6 x C-0.75%Ti
BS 409S19
10.5-12.5%Cr, <1%Ni, <1%Mn, <0.08%C, 6 x
C-1.0%Ti
DIN X6 CrTi 12 1.4512
10.5-12.5%Cr, <1%Ni, <1%Mn, <0.08%C, 6 x
C-1.0%Ti
JIS SUH 409
10.5-11.75%Cr, <0.5%Ni, <1%Mn, <0.08%C, 6
x C-0.75%Ti
Product Forms:
Plate,sheet & strip
EURONORM X6 CrTi 12 88-86/2
ASTM UNS S40900
409 176, 240, 480
BS 409S19 1449/2
DIN X6 CrTi 12
1.4512 17441
JIS SUH 409 4312
Tube and/or pipe DIN
X6 CrTi 12 1.4512 17455,
17456
ASTM UNS S40900
409 268
General
ISO 4955 4955 H1
ISO 683/13 1 Ti
EURONORM X6 CrTi 12 95-79
|
|
|